The Effect of Machine Parameters and the Composition of Additives in the Pelletization Process on the Physical and Mechanical Properties of Pellets in Se Chahoon Pelletization, Bafgh | |
| روش های تحلیلی و عددی در مهندسی معدن | |
| مقاله 3، دوره 14، شماره 41، دی 1403، صفحه 23-31 اصل مقاله (1.18 M) | |
| نوع مقاله: مقاله پژوهشی | |
| شناسه دیجیتال (DOI): 10.22034/anm.2024.21004.1627 | |
| نویسندگان | |
| Hossein Ali Lazemi* ؛ Abolfazl Ranjbar Bafghi | |
| Dept. of Mining Engineering, Islamic Azad University, Bafgh Branch, Bafgh, Iran | |
| چکیده | |
| Pelletization is a technique in which fine particles of iron ore concentrate are gradually mixed with lime and an adhesive (bentonite or fondue cement). These products are called raw pellets. These pellets must have standard metallurgical properties. Also, to prevent crushing during transportation, it must have sufficient physical and mechanical properties. In this research, the parameters affecting the pelletizing process, including the speed and rotation angle of the balling disc, the moisture content, the type and combination of the adhesive used, and the optimal conditions for the production of pellets with the desired dimensional characteristics and mechanical properties were determined. Bentonite and a combination of bentonite and Cement Fondu were used as an adhesive. The falling number and fracture strength tests were carried out on raw and dried pellets. Based on the results of the conducted experiments, the best pelletizing efficiency was recorded for a rotation angle of 40 degrees relative to the horizon, a rotation speed of 30 rpm, and a pelletizing duration of 60 minutes in the balling disc. The optimal moisture level in the moisture testing was around 9%. The increased bentonite content in the pellet showed an increasing/decreasing trend for the strength and falling number, and the highest strength was recorded for 3-4% bentonite content. The maximum compressive strength of dry pellets increased about six times compared to wet pellets with 9% moisture content. Using a mixture of Cement Fondu and bentonite in the pellets increases the strength. Still, after baking at high temperatures, lower strength was obtained compared to that of the pellet containing bentonite. Also, according to the results, the positive effect of increased fracture strength at high temperatures for the pellets made with a combination of 2% bentonite and 2% Cement Fondu is far less than pellets made with 3% bentonite and 1% Cement Fondu, while the same pellet showed an opposite result at ambient temperature. | |
| کلیدواژهها | |
| pellet؛ compressive strength؛ abrasion resistance؛ Cement Fondu؛ bentonite؛ pellet factory | |
| عنوان مقاله [English] | |
| The Effect of Machine Parameters and the Composition of Additives in the Pelletization Process on the Physical and Mechanical Properties of Pellets in Se Chahoon Pelletization, Bafgh | |
| نویسندگان [English] | |
| Hossein Ali Lazemi؛ َAbolfazl Ranjbar Bafghi | |
| Dept. of Mining Engineering, Islamic Azad University, Bafgh Branch, Bafgh, Iran | |
| چکیده [English] | |
| Pelletization is a technique in which fine particles of iron ore concentrate are gradually mixed with lime and an adhesive (bentonite or fondue cement). These products are called raw pellets. These pellets must have standard metallurgical properties. Also, to prevent crushing during transportation, it must have sufficient physical and mechanical properties. In this research, the parameters affecting the pelletizing process, including the speed and rotation angle of the balling disc, the moisture content, the type and combination of the adhesive used, and the optimal conditions for the production of pellets with the desired dimensional characteristics and mechanical properties were determined. Bentonite and a combination of bentonite and Cement Fondu were used as an adhesive. The falling number and fracture strength tests were carried out on raw and dried pellets. Based on the results of the conducted experiments, the best pelletizing efficiency was recorded for a rotation angle of 40 degrees relative to the horizon, a rotation speed of 30 rpm, and a pelletizing duration of 60 minutes in the balling disc. The optimal moisture level in the moisture testing was around 9%. The increased bentonite content in the pellet showed an increasing/decreasing trend for the strength and falling number, and the highest strength was recorded for 3-4% bentonite content. The maximum compressive strength of dry pellets increased about six times compared to wet pellets with 9% moisture content. Using a mixture of Cement Fondu and bentonite in the pellets increases the strength. Still, after baking at high temperatures, lower strength was obtained compared to that of the pellet containing bentonite. Also, according to the results, the positive effect of increased fracture strength at high temperatures for the pellets made with a combination of 2% bentonite and 2% Cement Fondu is far less than pellets made with 3% bentonite and 1% Cement Fondu, while the same pellet showed an opposite result at ambient temperature. | |
| کلیدواژهها [English] | |
| pellet, compressive strength, abrasion resistance, Cement Fondu, bentonite, pellet factory | |
| مراجع | |
|
[1] F. Zhang et al. (2019). Effect of basicity on the structure characteristics of chromium-nickel bearing iron ore pellets. Powder Technol.
[2] S.P.E. Forsmo et al. (2008). A study on plasticity and compression strength in wet iron ore green pellets related to real process variations in raw material fineness. Powder Technol.
[3] S.P.E. Forsmo. (2006). Binding mechanisms in wet iron ore green pellets with a bentonite binder. Powder Technol.
[4] Yonghe Ma, Qian Li. (2024). Reducing bentonite usage in iron ore pelletization through a novel polymer-type binder: Impact on pellet induration and metallurgical properties. Journal of Materials Research and Technology.
[5] Abdulmumini, M. M., (2016), The effect of pellets physical properties on handling pelleted biomass material in practical use. University of Greenwich.
[6] Eisele, T. and Kawatra, S., (2003). "A review of binders in iron ore pelletization". Mineral Processing Extractive Metallurgy Review.
[7] Yonghe Ma, Qian Li Xuling Chen,Yan Zhang, Yongbin Yang (2024), Qiang Zhong Reducing bentonite usage in iron ore pelletization through a novel polymer-type binder: Impact on pellet induration and metallurgical properties. Journal of Materials Research and Technology.
[8] S. K. Kawatra, T.C. Eisele, K.A. Lewandowski, and J.A.Gurtler (2007), “Novel binders and methods for agglomeration of ore” Technical Report, Michigan Technological University, Department of Chemical Engineering.
[9] O. Sivrikaya and A. I. Arol,(2011) “Pelletization of magnetite ore with colemanite added organic binders” Powder Technol.,Vol. 210.
[10] O. Sivrikaya and İ. Ali, (2012) “The bonding/strengthening mechanism of colemanite added organic binders in iron ore pelletization” International Journal of Mineral Processing,Vol. 111.
[11] S. P. E. Forsmo, P. O. Samskog, and B. M. T. Bjorkman, (2008) “A study on plasticity and compression strength in wet iron ore green pellets related to real process variations in raw material fineness” Powder Technol., Vol. 181, no. 3.
[12] Fallahi M, Soltanieh M, Adeli M, Farhani M, Spitzer K. H (2019). Investigation of the effect of pelletizing parameters on physical and mechanical properties of pellets prepared from Kahnouj ilmenite concentrate. Metallurgical Engineering.
[13] Kotta AB, Patra A, Kumar M, Karak SK (2020). Effect of molasses binder on the physical and mechanical properties of iron ore pellets.Int J Min Met Mater.
[14] Wang R, Zhang J, Liu Y, Zheng A, Liu Z, Liu X (2019), et al. Thermal performance and reduction kinetic analysis of cold-bonded pellets with CO and H2 mixtures. Int J Min Met Mater.
[15] Wang C, Xu C, Liu Z, Wang Y, Wang R, Ma L(2021). Effect of organic binders on the activation and properties of indurated magnetite pellets. Int J Min Met Mater.
[16] Linhares FM, Victor CCF, Lemos LR, Bagatini MC(2020). Effect of three different binders and pellet feed on granulation behaviour of sintering mixtures. Ironmak Steelmak.
[17] García, R., González-Vázquez, M., Martín, A., Pevida, C. and Rubiera, F. (2020). "Pelletization of torrefied biomass with solid and liquid bio-additives". Renewable Energ.
[18] T. C. Eisele and S. K. Kawatra (2003), “A review of binders in iron ore pelletization” Mineral Processing and Extractive Metallurgy Review.
[19] K. O. Ikebudu, Chukwumuanya E. O., Swift O. N. K., and Nwokeocha Toochukwu (2015), “Design of Pelletizing Machine (Balling Disc)”.
[20] M. Oorsprong (2018), “Iron ore pellets - determination of crushingstrength” Vol. 134313, no. 4, pp. 10–12.
[21] Gilvari, H., De Jong, W. and Schott, D. L. (2020). "The effect of biomass pellet length, test conditions and torrefaction on mechanical durability characteristics according to ISO standard 17831-1". Energies.
[22] Iljana, M., Kemppainen, A., Paananen, T., Mattila, O., Pisilä, E., Kondrakov, M. and Fabritius, T. (2015). "Effect of adding limestone on the metallurgical properties of iron ore pellets". International journal of mineral processing.
[23] Indra, A., Firdaus, R., Mulyadi, I. H. and Affi, J. (2020). "Enhancing the physical and mechanical properties of pellet-shaped hydroxyapatite by controlling micron-and nano-sized powder ratios". Ceramics International.
[24] Ma, Y., Liu, Y., Menon, C. and Tong, J. (2015), "Evaluation of wear resistance of friction materials prepared by granulation". ACS Applied Materials Interfaces,.
|
|
آمار
تعداد مشاهده مقاله: 200
تعداد دریافت فایل اصل مقاله: 110